D2 ( 1.2379 ) High Carbon Alloy Tool Steel Sheet ( Plate )

Wuxi Guanglu Special Steel Co., Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment

D2 ( 1.2379 ) High Carbon Alloy Tool Steel Sheet ( Plate )

  • 1
  • 2
  • 3

Brand Name : Daway

Model Number : D2, 1.2379, SKD11

Certification : SGS

Place of Origin : China

MOQ : 1 ton

Price : negotiable

Payment Terms : L/C, T/T

Supply Ability : 200 tons per month

Delivery Time : 15 days after receipt 30% of value

Packaging Details : seaworthy

Cold Work tool steel grade : D2, 1.2379, SKD11

Material : D2 ( 1.2379 ) tool Steel Sheet , Plate

Size : 1.5~20.0x850mm

Delivery state : annealed

Contact Now

D2 ( 1.2379 ) High Carbon Alloy Tool Steel Sheet ( Plate )

This air-hardening, cold work formulation features very high concentrations of carbon and

chromium (1.40 – 1.60% and 11.00 – 13.00%, respectively).

It’s highly wear-resistant and the high concentration of chromium imparts mild corrosion resistance.

APPLICATIONS: Rolls, punches, dies for blanking, forming, trimming, and thread rolling, shear knives,

food-processing knives, and gauges.

Material No. D2 Tool Steel - High-Carbon, High-Chromium, Cold-Work Steel

AISI/ASTM EN/DIN JIS
D2 1.2379, X155CrVMo12-1 SKD11

Chemical composition ( weight % )

Grade C Si Mn Cr Mo V
D2 1.50 0.30 0.30 12.00 0.75 0.90

Product forms

All tool steel D2 is sold as annealed condition, Size range

Thickness Width
1.5~20.0 850mm max.

HEAT TREATING INSTRUCTIONS
HARDENING
Critical Temperature:
Ac1: 1449°F (788°C) Ac3: 1553°F (845°C)
Ar1: 1418°F (769°C) Ar3: 1373°F (744°C)
Preheating: To minimize distortion and stresses in large or complex tools use a double preheat.
Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1150-1250°F (621-677°C) equalize,
then heat to 1400-1450°F (760-788°C). For normal tools, use only the second temperature range as a single preheating treatment.
Austenitizing (High Heat): Heat slowly from the preheat. Furnace or Salt: 1850-1875°F (1010-1024°C).
Quenching: Air or pressurized gas to 150-125ºF (66-51ºC).
Sizes up to 4 inches (101.6 mm) in thickness will through harden when air cooled from 1575ºF (857ºC).
Sizes up to 6 inches (152.4 mm) in thickness will through harden when air cooled from 1625ºF (885ºC).
Tempering: Temper immediately after quenching. Hold at temperature for 1 hour per inch (25.4 mm) of thickness,
2 hours minimum, then air cool to ambient temperature.
The typical tempering range is 350 to 400ºF (177 to 204ºC).
For maximum wear resistance, temper between 300-350°F (149-177°C) for a hardness of 62-64 HRC.
For the optimal balance between wear resistance and toughness, temper between 500-550°F (260-288°C).
This will produce 58-60 HRC.
For maximum toughness, double temper, 2 hours plus 2 hours, at temperatures above 950°F (510°C).
This will produce hardness of less than 58 HRC.
To minimize internal stresses in cross sections greater than 6 inches (152.4 mm) and to improve stability
in tools that will be EDM'd after heat treatment, soaking times of 4 to 6 hours at the tempering temperature
below 950°F (510°C) are strongly recommended.
Annealing: Annealing must be performed after hot working and before re-hardening.
Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1600-1650°F (871-899°C),
and hold at temperature for 1 hour per inch (25.4mm) of maximum thickness; 2 hours minimum.
Then cool slowly with the furnace at a rate not exceeding 50°F per hour (28°C per hour) to 1000°F (538°C).
Continue cooling to ambient temperature in the furnace or in air.
The resultant hardness should be a maximum of 255 HBW.

For Details, please Contact

WUXI GUANGLU Special Steel Co., Ltd.

Stainless martensitic • precipitation hardening steel • stainless ferritic — Our answer to your needs

Tel: +86 510 81812873

Email: export@guanglusteel.com

D2 ( 1.2379 ) High Carbon Alloy Tool Steel Sheet ( Plate )

Product Tags:

440c stainless steel

      

1.4021 stainless steel

      
Best D2 ( 1.2379 ) High Carbon Alloy Tool Steel Sheet ( Plate ) wholesale

D2 ( 1.2379 ) High Carbon Alloy Tool Steel Sheet ( Plate ) Images